Product Details
Production Description
3240 Epoxy Resin Glass Fiber Laminated Sheet is a composite material composed of woven fiberglass cloth with an epoxy resin and phenolic resin. It has high dielectric strength, radian resistance, high tensile strength, low cold flow or creep, dimension stability, low dissipation factor and high impact strength. Also, 3240 Epoxy Glass Fiber Laminate Board has great chemical resistance, so it can Withstand a variety of chemical solvents and acid erosion.
Application
This excellent properties of Epoxy Fiberglass Laminated Sheets 3240 alone with good processing characteristic make the materials apply into lots of industries. This material can be used in electrical equipment, aerospace condition, rocket cases, antenna insulators, test boards, end plates, cryogenic insulations, terminal boards, cutting model.
Technical Data for 3240 GradeB
NO |
TEST ITEMS |
UNIT |
TEST RESULT |
TEST METHOD |
1 |
Density |
g/cm3 |
2.07 |
GB/T 1303.2-2009 |
2 |
Water Absorption |
mg |
6.0 |
3 |
Bending Strength Perpendicular to Laminations |
A |
MPa |
203 |
B |
192 |
4 |
Modulus of Elasticity in Flexure |
A |
MPa |
2.12*104 |
B |
2.38*104 |
5 |
Parallel Layer Impact Strength
(Simply Supported Beam, Gap)
|
A |
KJ/m² |
47.4 |
B |
35.8 |
6 |
Parallel Layer Shear Strength |
A |
MPa |
49.8 |
B |
52.7 |
7 |
Tensile Strength |
A |
MPa |
147 |
B |
121 |
8 |
Compressive Strength Perpendicular to Laminations compressive |
MPa |
438 |
9 |
Insulation Resistance after Soaking |
Ω |
2.0*109 |
10 |
Vertical Layer Breakdown Voltage (90℃ + 2℃ oil, 20s step by step boost) |
MV/m |
8.6 |
11 |
Parallel Layer Breakdown Voltage (90℃ + 2℃ oil, 20s step by step boost) |
kV |
28.0 |
12 |
Flammability |
- |
V-1 |
13 |
Deflection Temperature under Load |
A |
℃ |
>140 |
B |
>140 |
14 |
Adhesive Strength |
N |
6324 |
GB/T 1303.6-2009 |
REMARK:
1. NO.2 the sample size is 50mm*50mm*50mm;
2. NO.8 the sample height is (9.05~9.56) mm;
3. NO.10 the sample thickness is (2.91~2.95)mm;
4. NO.11 the sample size is 100.00mm*5.08mm*24.10mm;
|
It can be machined to various shapes as insulation parts in which the mechanical and electrical properties is required.
Factory
|
|
two environmental control equipments used for the cyclic utilization of exhaust gas incineration afterheat
|
six domestically most advanced gum-dipping drying production equipments
|